SiCP／2024Al复合材料的阳极氧化研究
Anodizing Protection for SiC_P/2024Al Composite Material
查看参考文献11篇
|
文摘
|
为了研究SiCp／2024Al复合材料阳极氧化的保护效果，用电化学方法、浸泡试验和盐雾试验研究了该复合材料及相应的施加阳极氧化保护试样在3．5％NaCl溶液中的腐蚀行为，并用扫描电子显微镜（SEM）对腐蚀形貌和氧化膜的微观形态进行了观察。结果表明：SiCp／2024Al经过阳极氧化后在3．5％NaCl溶液中的耐蚀性明显提高，Ecorr和Epit正移150mV，Icorr从3．650μA减小到0．358μA，腐蚀速率由0．336mm／a下降到0．122mm／a；虽然SiC颗粒的存在影响了阻挡层的连续性，但多孔层仍能在电解质／材料界面不断生成，并且多孔层上的孔隙可以在封孔过程中得以闭合。 |
|
其他语种文摘
|
Corrosion be-haviors of SiCp/2024Al metal matrix composite material and the same materials with anodizing coating in 3. 5% NaCl solution were investigated by electrochemical method and immersion testand salt spray test, and the corrosion surface and morphology of oxide film were observed using XL30ESEMFEG - SEM. The re-sults show that the corrosion resistance of SiCp/2024Al increases notably in 3.5% NaCl solution after anodizing. En,r and E]A move 150 mV positively, Icm decreases from 3. 650 (jlA to 0. 358 |jlA , and the corrosion rate decreases from 0. 336 mm/a to 0. 122 mm/a accordingly. Though the barrier layer is discontinuous due to the presence of SiC particles, the porous layer can still form continuously on the interface of electrolyte and material, and the gaps in porous layer can be closed in subsequent sealing course. |
|
来源
|
材料保护
,2006,39(3):14-16 【核心库】
|
|
关键词
|
铝复合材料
;
阳极氧化
;
SiC
;
耐蚀性
;
阻挡层
;
多孔层
|
|
地址
|
1.
鞍山师范学院化学系, 辽宁, 鞍山, 114005
2.
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-1560 |
|
学科
|
一般工业技术 |
|
文献收藏号
|
CSCD:2342180
|
参考文献 共
11
共1页
|
|
1.
Metzger M. The influence of SiC reinforcement on pitting behavior of aluminum[J].
Ind Eng Chem Prod Res Dev,1983,22:296-305
|
CSCD被引
1
次
|
|
|
|
|
2.
Aylor D M. Assessing the corrosion resistance of metal matrix composite materials in marine environments[J].
Mater Performance,1984(7):32
|
CSCD被引
2
次
|
|
|
|
|
3.
Trazaskoma P P. Pit morphology of Al alloy and SiC/Al metal matrix composites[J].
Corrosion,1990,46(5):402-409
|
CSCD被引
2
次
|
|
|
|
|
4.
Manfeld F. Corrosion protection of Al alloys and Al-based metal matrix composites by chemical passivation[J].
Corrosion,1989,45(8):615-630
|
CSCD被引
1
次
|
|
|
|
|
5.
贺春林. 2024Al与SiC_p/2024Al复合材料的腐蚀与腐蚀控制研究.
金属学报,2001,37(8):865-872
|
CSCD被引
8
次
|
|
|
|
|
6.
Shahid M. Mechanism of film growth during anodizing of Al-alloy-8090/SiC metal matrix composite in sulphuric acid electrolyte[J].
Mater Sci,1997,32:3775
|
CSCD被引
1
次
|
|
|
|
|
7.
Manfeld F. Influence of processing variables on the corrosion susceptibility of metal-matrix composites[J].
Corrosion Science,1986,26(9):727
|
CSCD被引
1
次
|
|
|
|
|
8.
Trazaskoma P P. Corrosion behavior of SiC/Al metal matrix composites[J].
Electrochem Soc,1983,130(9):1804-1809
|
CSCD被引
4
次
|
|
|
|
|
9.
Kiourtsidis G. Stress corrosion behavior of aluminum alloy 2024Al/SiCP metal matrix composites[J].
Materials Science and Engineering,1998,248:165-172
|
CSCD被引
2
次
|
|
|
|
|
10.
Hihara L H. Corrosion of metal matrix composites[J].
International Materials Reviews,1994,39:245-256
|
CSCD被引
18
次
|
|
|
|
|
11.
Lin S. Corrosion protection of Al/SiC metal matrix composites by anodizing[J].
Science,1992,48:61-67
|
CSCD被引
1
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问