TiO2/Fe2O3核-壳粒子的制备及光学性能
Synthesis and optic character of TiO2/Fe2O3 core-shell particles
查看参考文献14篇
|
文摘
|
钛酸四丁酯(TBOT)水解产生的TiO2沉积在单分散准球形α-Fe2O3颗粒的表面,形成均匀、连续的核-壳结构.TiO2壳层的厚度约为30 nm.在500℃热处理后,TiO2壳层从非晶态转变为锐钛矿结构.在光激发下,TiO2/Fe2O3核-壳粒子的电子从TiO2价带跃迁到能量较低的α-Fe2O3导带,在可见光区产生新的强吸收峰.光谱计算结果表明TiO2价带与α-Fe2O3导带的能量差为1.6 eV. |
|
其他语种文摘
|
A continuous uniform layer of amorphous TiO2 obtained by the hydrolysis of TBOT could be deposited on the surface of monodispersed pseudo-spherical a- Fe2O3. The thickness of the TiO2 shell was about 30 nm. After heat treatment at 500 "C, the structure of TiO2 shell transformed to the anatase. The UV-Vis spectrum of core-shell particles showed that the electron, induced by UV-Vis ray, transferred from the valence band of TiO2 to the conduction band of a-Fe2C>3. As a result, the absorb peak of core-shell particles shifted toward long wave, and the maximum absorbance appeared in the range of visible ray area. |
|
来源
|
材料研究学报
,2005,19(4):343-348 【核心库】
|
|
关键词
|
复合材料
;
单分散
;
准球形α-Fe2O3
;
锐钛矿TiO2
;
核-壳粒子
|
|
地址
|
1.
东北大学, 辽宁
2.
中国科学院金属研究所, 辽宁
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-3093 |
|
学科
|
物理学;一般工业技术 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:2027141
|
参考文献 共
14
共1页
|
|
1.
Frank Caruso. Mater.
Chem Mater,1999,11:3394
|
CSCD被引
11
次
|
|
|
|
|
2.
A Quirantes. Colloid.
J. Colloid. Interf. Sci,1997,189(2):236
|
CSCD被引
5
次
|
|
|
|
|
3.
Wan Peter Hsu. Colloid.
J. Colloid. Interf. Sci,1993,156(1):56
|
CSCD被引
4
次
|
|
|
|
|
4.
Manuel Oca(n)a.
Langmuir,1991,7:2911
|
CSCD被引
1
次
|
|
|
|
|
5.
Masahiro Ohmori. Colloid.
J. Colloid. Interf. Sci,1992,150(2):594
|
CSCD被引
22
次
|
|
|
|
|
6.
Bar Aiken. Colloid.
J. Colloid. Interf. Sci,1988,126(2):645
|
CSCD被引
4
次
|
|
|
|
|
7.
Ikram ul Haq. Colloid.
J. Colloid. Interf. Sci,1997,192(1):104
|
CSCD被引
3
次
|
|
|
|
|
8.
Ajay Garg. Colloid.
J. Colloid. Interf. Sci,1988,126(1):243
|
CSCD被引
4
次
|
|
|
|
|
9.
A Fujishima. Photochemistry Reviews.
Journal of Photochemistry and Photobiology C: Photochemistry Reviews,2000,1:1
|
CSCD被引
596
次
|
|
|
|
|
10.
Ulrike Diebold. Surface Science Report.
Surface Science Report,2003,48:53
|
CSCD被引
236
次
|
|
|
|
|
11.
王艳芹. 二氧化钛和三氧化二铁复合纳米晶电极的光电化学性质.
物理化学学报,1999,15(3):222
|
CSCD被引
24
次
|
|
|
|
|
12.
Paola Gherardi. Colloid.
J. Colloid. Interf. Sci,1986,57(1):109
|
CSCD被引
1
次
|
|
|
|
|
13.
Xintong Zhang.
Thin Solid Films,1998,568:327-329
|
CSCD被引
1
次
|
|
|
|
|
14.
Noshir S Pesika. Mater.
Adv. Mater,2003,15(15):1288
|
CSCD被引
2
次
|
|
|
|
|
了解气象卫星更多信息，请访问