文摘
|
在多孔阳极氧化铝(AAO)模板中分别沉积金属镍(Ni)、钴(Co)，制备了Ni/AAO和Co/AAO纳米有序阵列复合结构，对其光吸收特性进行了比较研究。实验结果表明，相同结构参量的模板中，Ni、Co纳米粒子的表观形状随沉积时间的变化规律基本一致，但Co/AAO及Ni/AAO复合结构的光吸收特性却有较大差异。Ni/AAO复合结构表现出间接带隙半导体的光学特征，而Co/AAO复合结构具有直接带隙半导体的光学特征。同时，随金属沉积量的增加，Ni/AAO吸收边的红移量仅约为13 nm，而Co/AAO复合结构的吸收边红移量却超过了80 nm。用Maxwell-Garnett(M-G)理论分析了导致二者光吸收特性存在较大差异的主要原因。 |
|
其他语种文摘
|
Ordered Ni/AAO and Co/AAO nano-array composite structure are prepared via electrodeposition of the metal within the process of anodically-grown porous anodic aluminum oxide (AAO) membranes. The optical properties of the two composite are studied. The results show that the difference between the Ni/AAO and Co/AAO are very large. Although the micrograph of the Ni nano-particles and the Co nano-particles are nearly the same, as the metal composition increasesd. the absorption band-edge of the Ni/AAO composite is small red-shifted (13 nm). However, the absorption band-edge of the Co/AAO composite is strongly red-shifted (80 nm). Meanwhile, the Ni/AAO and Co/AAO composite exhibit the optical features of the semiconductor with indirect and direct band gap respectively. |
|
来源
|
光学学报
,2005,25(1):77-82 【核心库】
|
|
关键词
|
材料
;
纳米有序阵列
;
光吸收特性
;
吸收边
|
|
地址
|
1.
西北师范大学物理与电子工程学院, 甘肃, 兰州, 730070
2.
中国科学院兰州化学物理研究所, 固体润滑国家重点实验室, 甘肃, 兰州, 730000
3.
兰州大学化学化工学院, 甘肃, 兰州, 730000
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0253-2239 |
|
学科
|
物理学 |
|
基金
|
甘肃省自然科学基金
;
西北师范大学知识与科技创新工程
|
|
文献收藏号
|
CSCD:1881092
|
了解气象卫星更多信息，请访问