用柠檬酸溶胶凝胶法合成SrFeCo0.5Ox氧化物
Synthesis of Complex Conducting Oxides SrFeCo_(0.5)O_x by Citrates Solgel Method
查看参考文献13篇
|
文摘
|
采用柠檬酸溶胶凝胶法合成SrFeCo0.5Ox混合导体氧化物，利用XRD、TEM以及DTA方法研究与分析了不同条件下样品的晶体结构组成、相貌。确定了最佳制备条件。结果说明在燃料剂／氧化剂比例为0.64,550℃时得到单相钙钛矿氧化物，氧化物为纳米球形颗粒，尺寸分布均匀；加热温度升高850℃晶体结构无变化，颗粒尺寸明显长大但是形状不变，同时分析了溶胶凝胶反应过程及影响因素。 |
|
其他语种文摘
|
Conducting oxides SrFeCo_(0.5)O_x powder was prepared by nitrate sol-gel method. Thermal reaction of the gel during heating is investigated by DTA and the crystal structure and morphology of the calcined powder were characterized by .r-ray diffraction (XRD) and transmission electron microscope (TEM) respectively. The results show that single perovskite oxide can be formed at 550℃ with x= 0.64. The oxide size particle is in nanometer grade and very uniform. As the calcined temperature increases up to 850℃ , the phase of the sample still does not change but the particles size becomes 100 mm. The polymerization reaction of nitrates sol-gel is also discussed. |
|
来源
|
东北大学学报. 自然科学版
,2003,24(1):61-63 【核心库】
|
|
关键词
|
柠檬酸溶胶凝胶法
;
无机合成
;
混合导体氧化物
;
SrFeCo0.5Ox
;
晶体结构
;
制备条件
;
锶
;
铁钴氧化物
|
|
地址
|
1.
东北大学材料与冶金学院, 辽宁, 沈阳, 110004
2.
中国科学院金属研究所, 辽宁, 沈阳, 110014
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-3026 |
|
学科
|
化学 |
|
基金
|
国家973计划
|
|
文献收藏号
|
CSCD:1282878
|
参考文献 共
13
共1页
|
|
1.
Balachandran U.
Appl Catal,1995,133(1):19-29
|
CSCD被引
34
次
|
|
|
|
|
2.
Ma B.
Solid State Ionics,1996,83(1):65-71
|
CSCD被引
12
次
|
|
|
|
|
3.
Ma B.
Solid State Ionics,1997,100(1):52
|
CSCD被引
1
次
|
|
|
|
|
4.
Kim S.
Solid State Ionics,1999,109(1-2):187-196
|
CSCD被引
4
次
|
|
|
|
|
5.
Armstrong T.
J Electrochem Soc,2000,147(2):435-438
|
CSCD被引
4
次
|
|
|
|
|
6.
Prado F.
J Electrochem Soc,2001,148(4):J7-J14
|
CSCD被引
4
次
|
|
|
|
|
7.
霍地. 混合导体氧化物SrFeCo_(0.5)O_(3-x)的微波混合加热合成.
东北大学学报（自然科学版）,2002,23(4):359-362
|
CSCD被引
1
次
|
|
|
|
|
8.
Pechini M.
Method of preparing lead and alkaline-earth titanates and niobates and coatingmethod using the same to form a capacitor.U S Paten 3330697,1967
|
CSCD被引
1
次
|
|
|
|
|
9.
Paul A Lessing.
Ceramic Bulletin,1989,68(5):1002-1007
|
CSCD被引
11
次
|
|
|
|
|
10.
Zeng Y.
J Mater Sci,2001,36(5):1271-1276
|
CSCD被引
6
次
|
|
|
|
|
11.
Fjellvag H.
J Mater Chem,1997,7(12):2415-2419
|
CSCD被引
3
次
|
|
|
|
|
12.
.
ICDD Powder Diffraction File Card No.34-638.International centre for diffraction data
|
CSCD被引
1
次
|
|
|
|
|
13.
Sukumar Roy.
J Mater Res,1999,14(4):1524-1531
|
CSCD被引
4
次
|
|
|
|
|
了解气象卫星更多信息，请访问