文摘
|
利用交流阻抗测试技术、扫描电镜及表面能谱、失重法、微生物分析等方法，在室内模拟条件下研究了海泥中硫酸盐还原菌对碳钢腐蚀的影响，及在含和不含硫酸盐还原菌的海泥构成的宏电池腐蚀中碳钢的腐蚀行为。180天的试验结果表明，在有菌泥中碳钢的自然腐蚀速度均大于在灭菌泥中，两者相差3.5倍。说明海泥中硫酸盐还原菌增大了碳钢的腐蚀速率。在有菌和灭菌海泥中构成宏电池时，有菌海泥中碳钢作为阳极，腐蚀速率比自然腐蚀状态下有所增大，加速率为11.9％。而在灭菌海泥中碳钢作为阴极，腐蚀速率比自然腐蚀状态下有所减小。 |
|
其他语种文摘
|
The effect of Sulfate Reducing Bacterial (SRB) on corrosion of carbon steel in seamud, and macrocell corrosion induced by seamuds with SRB and without SRB of carbon steel have been studied by using bacterial analyses, weight loss, Electrochemical Impedance Spectroscopy, Scanning Electron Microscopy (SEM) and EDXA.The corrosion rate of carbon steel in seamud with SRB was 3.5 times of those in seamud without SRB. Within a marocell consisted with seamud with and without SRB, the part of carbon steel immersed in seamud with SRB plays as anode, thus exhibits corrosion rate higher than that of free corrosion immersed in the same mud. |
|
来源
|
腐蚀科学与防护技术
,2003,15(2):104-106 【核心库】
|
|
关键词
|
碳钢
;
海泥
;
硫酸盐还原菌
;
微生物腐蚀
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-6495 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
国家科技基础性工作专项重点项目
|
|
文献收藏号
|
CSCD:1279272
|
|
|
1.
李异.
腐蚀科学与防护技术,1991,3(1):22
|
CSCD被引
9
次
|
|
|
|
|
2.
野中英正.
防蚀技术,1989,38(1):53
|
CSCD被引
1
次
|
|
|
|
|
3.
Rger A King.
Material Performance,1980,19(1):39
|
CSCD被引
1
次
|
|
|
|
|
4.
Olowe A A.
J Corrosion,1989,45(3):229
|
CSCD被引
2
次
|
|
|
|
|
5.
郭公玉.
电化学,2001,7(4):461
|
CSCD被引
2
次
|
|
|
|
|
6.
郭琦龙. 碳钢在海泥中的电化学行为.
中国腐蚀与防护学报,1999,19(5):315
|
CSCD被引
3
次
|
|
|
了解气象卫星更多信息，请访问