Ni25Al75合金快速凝固过程中的包晶反应与凝固进程
Peritectic reaction and solidification path in Ni-Al alloy during rapidly solidificaiton process

查看参考文献12篇

巴发海 1   沈宁福 2   虞钢 1  
文摘 用平面流铸技术制备了Ni25Al75合金条带，利用XRD，TEM和EDS对快速凝固后的显微组织和微区成分进行了分析。研究表明，Ni—A1合金快速凝固过程中的包晶反应受到了很大程度的抑制，从而影响到快速凝固进程，造成最终相组成中出现了平衡条件下不可能出现的α(A1)，并使NiAl3相有效合金浓度和生长速度增加，导致最终相组成中NiAl_3相质量分数增加。
其他语种文摘 Rapidly solidified ribbons of NJ25 A17S were prepared by planar flow casting. The microstructure of the ribbons was investigated by XRD, TEM and EDS. The results show that the peritectic reaction is restrained to great extent during continuous cooling in rapid solidification, which has an significant effect on solidification path. a( Al) occurs in the microstructure of the ribbon, which is impossible in equilibrium condition. The effective alloy concentration and growth velocity of NiAl_3 phase are increased, which leads to the increase of the mass fraction of NiAl_3 phase.
来源 中国有色金属学报 ,2003,13(2):335-338 【核心库】
关键词 Ni25Al75合金 ; 快速凝固 ; 包晶反应 ; 平面流铸技术 ; 显微组织 ; 微区成分
地址

1. 中国科学院力学研究所, 非线性力学国家重点实验室, 北京, 100080  

2. 郑州大学材料研究中心, 郑州, 450002

语种 中文
文献类型 研究性论文
ISSN 1004-0609
学科 金属学与金属工艺
基金 国家自然科学基金
文献收藏号 CSCD:1279235

参考文献 共 12 共1页

1.  Pohla C. Acta Mater,1997,45(5):2155-2162 CSCD被引 2 次    
2.  巴发海. 金属学报,2001,37(8):846-851 CSCD被引 5 次    
3.  Shen Ningfu. Proc the Third PRICM on Advanced Material and Processing,1998:2405-2412 CSCD被引 2 次    
4.  Shen Ningfu. Effects of Solidification Kinetics on the Phase Composition in Ni-Al System. Journal of Zhengzhou University of Technology,2000,21(2):1-8 CSCD被引 3 次    
5.  Assadi H. Acta Mater,1998,46(2):491-454 CSCD被引 3 次    
6.  巴发海. 测定Ni-Al合金XRD相组成用纯NiAl_3的制备工艺. 钢铁研究学报,2000,12(5):66-69 CSCD被引 2 次    
7.  Shao G. Acta Mater,1994,42(9):2937-2940 CSCD被引 3 次    
8.  巴发海. 快速凝固Ni-Al合金的相组成和凝固动力学研究,2001:25-30 CSCD被引 3 次    
9.  巴发海. 中国有色金属学报,2002,12(5):878-881 CSCD被引 2 次    
10.  Trivedi R. International Materials Reviews,1994,39:49-74 CSCD被引 41 次    
11.  Boettinger W J. Rapid Solidification Processing: Principle and Technology,1988:13 CSCD被引 1 次    
12.  Afred G. Metallurgical and Materials Transactions A,1998,29:3047-3056 CSCD被引 1 次    
引证文献 1 篇

1 李芸 过冷Co_(75)B_(25)合金的凝固 金属学报,2018,54(8):1165-1170
CSCD被引 1 次

显示所有1篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护：中国科学院文献情报中心
地址：北京中关村北四环西路33号 邮政编码：100190 联系电话：(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号