镍基高温合金的真空感应熔炼脱氢
Deoxidation during vacuum induction melting of Ni-base superalloy
查看参考文献10篇
|
文摘
|
研究了在真空感应炉中使用CaO坩埚熔炼镍基高温合金的脱氧效果，分析了加入0.02%C和0.5Al对脱氧的影响，初步进行了在CaO坩埚中脱氧反应的热力学计算。研究表明：熔化期可以脱除大部分的氧；采用CaO坩埚，选择合适的熔炼工艺及C和Al加入量，可使氧的含量降低到小于0.0006%。 |
|
其他语种文摘
|
The deoxidation effect in vacuum induction melting of Ni-base superalloy by using CaO crucible was studied. The influ ence of adding 0.02 % C and 0. 5% Al on deoxidation was also analyzed. Thermodynamics calculation of the deoxidation reaction ii CaO crucible was done. The results show that most oxygen can be removed in melting period. In CaO crucible, adopting proper melt ing technology and carbon and aluminium addition amounts, oxygen content could be reduced to below 0.000 6%. |
|
来源
|
中国有色金属学报
,2002,12(2):217-220 【核心库】
|
|
关键词
|
镍基高温合金
;
真空感应熔炼
;
脱氧
;
氧化钙坩埚
|
|
地址
|
中国科学院金属研究所, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1004-0609 |
|
学科
|
冶金工业 |
|
文献收藏号
|
CSCD:1135701
|
参考文献 共
10
共1页
|
|
1.
陈荣章.
材料工程,1995,8:3-12
|
CSCD被引
61
次
|
|
|
|
|
2.
刘奎.
金属学报,1995,3(Suppl):370-373
|
CSCD被引
7
次
|
|
|
|
|
3.
李守军.
金属学报,1995,3(Suppl):175-179
|
CSCD被引
1
次
|
|
|
|
|
4.
Halali M.
Superalloys 1996,1996:457
|
CSCD被引
1
次
|
|
|
|
|
5.
Jones W E.
Vacuum metallurgy,1957,5:189-192
|
CSCD被引
1
次
|
|
|
|
|
6.
Degawa T.
Tetsu to Hagane,1987,14:1691-1697
|
CSCD被引
2
次
|
|
|
|
|
7.
孙长杰.
金属学报,1998,7:731-734
|
CSCD被引
2
次
|
|
|
|
|
8.
刘彦海.
耐火材料,1998,32(3):149-150
|
CSCD被引
14
次
|
|
|
|
|
9.
Chen Fuwang.
Materials Letter,1998,34:372-376
|
CSCD被引
18
次
|
|
|
|
|
10.
Bates P.
Steel Times,1995,7:268-269
|
CSCD被引
1
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问