316不锈钢在F^-/Cl^-酸性溶液中的腐蚀行为
Corrosion Behavior of 316 Stainless Steel in Solutions Containing F~-/Cl~- Ions
查看参考文献10篇
|
文摘
|
用电化学测量技术，对含F^-和Cl^-稀醋酸介质中316不锈钢的腐蚀行为进行了研究。结果表明，316不锈钢在低浓度F^-/Cl^-稀醋酸溶液中能够钝化，致密钝化膜为双层结构；F^-能加速其均匀腐蚀，但加速作用不显著，浓度不同的含F^-稀醋酸介质中均无点蚀。 |
|
其他语种文摘
|
The corrosion behavior of 316 stainless steel (316SS) in dilute acetic acid solutions containing fluo-ride/chloride ions was investigated by using electrochemical measurement techniques. It was found that 316 could be passivated in 0.1 mol/L HAc solution mixed with 0.001 mol/L NaF and 0.001mol/L NaCl or with 0～0.1 mol/L NaF. The well passivated films had an internal chromium oxide rich layer and an external iron oxide rich layer.The results revealed that F~- could increase corrosion rate slightly for 316SS in 0.1 mol/L HAc solution. No pitting corrosion occurred in the various tested solutions. The corrosion rate of 316SS increased with increas-ing the temperature of solutions containing F~-/Cl~- ions, but 316SS was still in the passive state at 80 ℃ . |
|
来源
|
中国腐蚀与防护学报
,2002,22(3):162-166 【核心库】
|
|
关键词
|
酸性溶液
;
不锈钢
;
腐蚀
;
电化学阻抗谱
;
燃烧电池
;
PEMFC
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-4537 |
|
学科
|
电工技术 |
|
基金
|
国家973计划
|
|
文献收藏号
|
CSCD:1133328
|
参考文献 共
10
共1页
|
|
1.
Murphy O J.
Electrochim. Acta,1998,43(24):3829-3840
|
CSCD被引
12
次
|
|
|
|
|
2.
Davies D P.
Appl. Electrochem,2000,30:101-105
|
CSCD被引
24
次
|
|
|
|
|
3.
Hornung R.
J. Power Sources,1998,72:20-21
|
CSCD被引
18
次
|
|
|
|
|
4.
Strehblow H H.
Werkstoffe und Korrosion,1984,35:437-448
|
CSCD被引
4
次
|
|
|
|
|
5.
Sekine I.
Corros. Sci,1994,36(8):1411-1424
|
CSCD被引
4
次
|
|
|
|
|
6.
MacDonald D D.
J. Electrochem. Soc,1973,120(3):317-324
|
CSCD被引
2
次
|
|
|
|
|
7.
Wu X J.
J. Electrochem. Soc,1999,146(5):1847-1853
|
CSCD被引
15
次
|
|
|
|
|
8.
Schultze J W.
Electrochim. Acta,2000,45:2499-2513
|
CSCD被引
34
次
|
|
|
|
|
9.
Yang M Z.
J. Electrochem. Soc,1999,146(6):2107-2112
|
CSCD被引
6
次
|
|
|
|
|
10.
Montemor M F.
Corros. Sci,2000,42:1635-1650
|
CSCD被引
33
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问